| Mechanical Properties | Method | Value | Rating |
|---|---|---|---|
| Tensile modulus (Young's modulus) | ISO 527-1 | 3100 MPa | Excellent |
| Tensile strength at yield | ISO 527-1 | 47 MPa | Typical |
| Tensile stress at break | ISO 527-1 | 22 MPa | Typical |
| Elongation at break | ISO 527-1 | 30 % | Good |
| Flexural modulus | ISO 178 | 3200 MPa | Excellent |
| Flexural strength | ISO 178 | 65 MPa | Good |
| Charpy notched impact strength (+23°C) | ISO 179-1eA | 12 kJ/m² | Very Good |
| Charpy unnotched impact strength (+23°C) | ISO 179-1eU | 228 kJ/m² | Outstanding |
| Thermal Properties | Method | Value | Rating |
|---|---|---|---|
| Heat deflection temp. (HDT/B) — 0.45 MPa | ISO 75-1 | 55 °C | Typical |
| Vicat softening temp. (VST/B50) | ISO 306 | ~100 °C | Very Good |
| Melting point (Tm) | ISO 3146-C | 150–170 °C | - |
| Glass transition temp. (Tg) | ISO 11357-1 (DSC) | ~65 °C | Typical |
| Melt volume rate (MVR) — 235°C/5.0 kg | - | 2 cm³/10 min | Typical |
| Thermal decomposition temp. | - | ~230 °C | Typical |
| CLTE — flow direction | - | 0.65 cm/cm/°C | Very Good |
| Physical Properties | Method | Value | Rating |
|---|---|---|---|
| Density | ISO 1183-1 | 1.3 g/cm³ | - |
| Water absorption (saturation, 23°C) | - | 0.8 % | - |
| Mould shrinkage | ISO 294-4 | 0.8 % | Typical |
| Special Properties | Method | Value | Rating |
|---|---|---|---|
| UV resistance | - | Moderate | - |
| Chemical resistance | - | Moderate | - |